Should the surfaces of flanges be coated to prevent corrosion? Why or why not?


Selected Answers

From bart de cremer of acotec nv on December 20, 2016:
Of course, flanges should be coated wit a solvent-free epoxy to prevent corrosion and rust creep.

From Sal Bustos of MWD on December 19, 2016:
The answer is Yes and No. As a coater/applicator, and now manager, I've seen both coated and uncoated flanges on water-deliver systems with raw and treated water. Most notable were on the older systems where flanges were coated with a red lead primer. With that said, I'd say coat the exposed portion of the flange with an appropriate coating for the service condition and leave the gasket sealing area bare or coat lightly with a zinc coating. The thought here is, generally, a gasket grease is applied and the bolt-down pressure will seal as well as any coating applied, thus keeping oxygen out and corrosion to a minimum.

From Paiboonsak Saengsomboon of JT Marketing Co., Ltd. on December 15, 2016:
It is necessary to coat the flange's face  to prevent the crevice corrosion.

From Warren Brand of Chicago Coatings Group on December 13, 2016:
Having worked on 100s, perhaps 1000s of projects involving flange and manhole faces, we tend to coat the faces for the same reasons William mentioned. We tend to apply the coating system a bit thicker on the flange face in case the owner needs to lightly sand the coating system to make it smooth and/or perfectly flush. Of course, the edge of the flange face is critical and we usually stripe coat that right angle, before coating the face.

From Per Gabrielsson of Free Lance Consultations and Inspections on December 13, 2016:
If the flange face is coated with multiple layers, tightening problems may occur and the coatings may split. A single coat, for instance, of 1-component, high-zinc-content polyurethane would be a reasonably good solution (does not require a blasted, rugged profile as inorganic zinc does).

From William Slama of International Paint/Ceilcote Products on December 12, 2016:
We have encountered this many times in the past where flanges get severe corrosive attack. For some reason, some plant people or applicators do not want to coat (or line) flange faces. To me, that is unbelievable. One must look only at the effectiveness and actual expected sealing area that the gasket accomplishes. At the very least, there will be a line at the edge of the flange that is exposed to the chemical solution. More likely, the actual "sealing" line will be a bit out onto the flange. Given that the flange face can easily be coated or lined, I don't see any reason not to line them with the same system used in the vessel.


Please sign in to submit your answer this question

   

Tagged categories: Corrosion; Corrosion control coatings; Corrosion protection


Current PSF Question | Submit a PSF Question | Full PSF Archive

 
 
 

Technology Publishing Co., 1501 Reedsdale Street, Suite 2008, Pittsburgh, PA 15233

TEL 1-412-431-8300  • FAX  1-412-431-5428  •  EMAIL webmaster@durabilityanddesign.com


The Technology Publishing Network

Durability + Design PaintSquare the Journal of Protective Coatings & Linings Paint BidTracker

 

© Copyright 2012-2019, Technology Publishing Co., All rights reserved